Iron 450-10 Ductile Iron Casting Parts , Heat Treatment Metal Casting Parts
|Place of Origin:||DONGGUAN CHINA|
Payment & Shipping Terms:
|Minimum Order Quantity:||3000|
|Packaging Details:||Export standard packing|
|Delivery Time:||15 days|
|Payment Terms:||L/C, T/T, Western Union|
|Material:||Alloy Cast Iron||Tolerance:||±0.01mm|
|Used For:||Machinery Accessories||Process:||CNC Machines, Machining Center, Lathe, Milling Machine, Drilling Machine, Etc.|
|Surface:||Paint Coating, Electrophoretic Coating, Electric Galvanized Coating||Packing:||Export Standard Packing|
iron casting parts,
metal casting parts
OEM nodular cast iron parts CNC casting processing services
Product Description and Process
The product description and processes:
1. OEM nodular cast iron parts CNC machining parts supplier in China
2. The production process:
Green sand casting process
Precoated sand casting process
Resin sand casting process
3. Weight range: we can produce 50 g to 2000 kilograms of cast iron castings
4. Mold production: manual, forming machine, shell molding machine, automatic molding line.
5. Processing: CNC machine tools, machining center, lathe, milling machine, drilling machine, etc.
6. Surface treatment: paint coating, electrophoretic coating, electric galvanized coating, black oxide coating, phosphating coatings, powder coatings, etc.
Product materials and USES:
1. Usually use grey iron HT200, HT250, nodular cast iron 12, 60-65-45-40 - reached 18-55-06 reached 60-03 - production, etc.
2. Nodular cast iron products are widely used in automobiles, trains, trucks, auto parts, mining machinery parts, agricultural machinery parts, textile machinery parts, engineering machinery parts, etc.
Ductile iron is what?(of)
If you want to for chemical analysis of nodular cast iron, this is what you will usually find:
Iron ~ 94%
Carbon 3.2 -3.60%
Silicon 2.2 -2.8%
Manganese 0.1- 0.2%
Magnesium 0.03- 0.04%
P 0.005- 0.04%
Sulfur 0.005- 0.02%
Copper < = 0.40%
In order to improve the strength of the nodular cast iron, can add additional tin or copper.In order to improve the corrosion resistance, copper, nickel and chromium alternative to 15-30% of iron.
Common level of nodular cast iron:
Although there are many different nodular cast iron specifications, foundry usually provide three kinds of common brand;
|Physical and Mechanical Properties||ASTM A536, Grade 60-40-18||ASTM A536, Grade 65-45-12||
ASTM A536, Grade
|Tensile Strength, min, psi||60000||65000||80000|
|Tensile Strength, min, MPa||414||448||552|
|Yield Strength, min, psi||40000||45000||55000|
|Yield Strength, min, MPa||276||310||379|
|Elongation in 2 in. or 50 mm, min %||18||12||6|
|Melting Temperature (Degrees F)||2,100 - 2,190||2,100 - 2,190||2,100 - 2,190|
|Melting Temperature (Degrees C)||1,150 - 1,200||1,150 - 1,200||1,150 - 1,200|
|Compressive Strength Ksi||429||429||429|
|Compressive Strength MPa||2960||2960||2960|
Ductile iron castings:
Nodular cast iron was invented by the middle of the twentieth century synthesis of metal material, is a kind of used in the manufacture of cast iron.Cast iron technology of molten iron and metal material, has the ductility.
Ductile iron process must start from the production of ductile iron, nodular cast iron is formed by adding small amounts of other elements into the iron, so that the carbon ball instead of thin sheet.This enables the material to without destroying situation to change.Usually, nodular cast iron has a higher tensile strength than that of gray cast iron, grey cast iron is traditionally used in the manufacture of iron cast iron products.Nodular cast iron, as the name implies, than the traditional more malleable iron material, the traditional iron materials tend to be more brittle, easy to fracture under high tensile stress.Ductile iron is usually used in the manufacture of cast iron pipe, the use of the water and sewer.Nodular cast iron used in many various applications in different industries.These industries include, but are not limited to agriculture, automobile, irrigation, ventilation, hydraulic pressure.
We can provide:
Material: alloy steel, carbon steel, stainless steel, malleable cast iron, grey cast iron, ductile iron, aluminum bronze, etc
Process: precision casting, sand casting, resin sand casting, green sand casting), permanent casting, die casting, centrifugal casting, forging, stamping and so on.
Ductile Iron Casting Metal Parts ±0.01mm Tolerance 50 G To 2000 Kilograms Images